RENDEMEN SELULOSA HASIL EKSTRAKSI BATANG TANAMAN JAGUNG (Zea mays) MENGGUNAKAN VARIASI LAMA BLANCHING DAN KONSENTRASI NaOH

Abstract

The aim of this study to determine the effect of NaOH concentration on cellulose extraction process from corn stalks to its yield and physical properties of cellulose. Method of study included: extraction of corn plant cellulose through processed of delignification, washed, blanched, dried and grinded of cellulose powder. The experiment used the extraction time for 60 minutes with the concentration of NaOH with 5 treatment level that was 10%, 15%, 20%, 25% and 30%. Each treatment was repeated three times and each was analyzed with two replications. The experimental unit obtained 3x5x2 = 30 units of experiment. Physical cellulose product analysis included measurement of yield, pH, Water Holding Capacity (WHC) and Oil Holding Capacity (OHC). The results showed that the use 10% NaOH concentration obtained yield of 32.41%; pH value of 8.33; water holding capacity (WHC) was 7.8 g/g; the oil holding capacity (OHC) was 8.33 g/g and water content was 7.96%
Keywords: Blanching, cellulose, stalks of corn plants, extraction, Sodium Hydroxide
ABSTRAK
Selulosa merupakan salah satu senyawa polimer yang dapat disintesis dari bahan-bahan tanaman, termasuk limbah kegiatan pertanian antara lain batang singkong, jerami, tandan kosong kelapa sawit, tongkol jagung dan batang tanaman jagung. Tujuan penelitian ini adalah untuk mengetahui pengaruh konsentrasi NaOH dan lama waktu delignifikasi pada proses ekstraksi selulosa dari batang tanaman jagung. Metode ekstraksi selulosa diawali dengan proses penyiapan bahan batang tanaman jagung, proses delignifikasi, pencucian, blanching, pengeringan dan pembuatan serbuk selulosa. Rancangan percobaan yang digunakan yaitu rancangan acak lengkap dengan dua faktor perlakuan dan dua ulangan. Lama waktu (T) dengan 3 taraf perlakuan, yaitu: T1= 60 menit, T2= 90 menit dan T3= 120 menit serta konsentrasi NaOH (K) dengan 5 taraf perlakuan yaitu K1= 10%, K1= 15%, K2= 20%, K3= 25% dan K4= 30%. Masing-masing perlakuan diulang dua kali. Sehingga diperoleh unit percobaan 3x5x2 = 30 unit percobaan. Analisis produk selulosa secara fisik dan kimia meliputi analisis pengukuran rendemen, kadar air, pH, analisis Water Holding Capacity (WHC) dan Oil Holding Capacity (OHC). Penggunaan NaOH konsentrasi 10% dengan waktu blanching 60 menit dapat digunakan pada proses ekstraksi selulosa batang jagung yang menghasilkan rendemen tertinggi sebesar 32,41% nilai pH 8,33; WHC rata-rata 7,8 g/g; OHC rata-rata 8,33 g/g dan kadar air rata-rata 7,96%
Kata kunci: Batang tanaman jagung, Blanching, Ekstraksi, NaOH, Selulosa
.PENDAHULUAN
Limbah organik dari kegiatan pertanian memiliki kandungan